|Place of Origin:||CHINA|
|Certification:||CE、 FDA 、CFDA、KFDA|
|Delivery Time:||10 working days after received your payment|
|Density Before Sintering (g/cm3):||3.1±0.5 G/cm3||Density After Sintering (g/cm3):||6.08±0.01 G/cm3|
|CTE After Sintering (25-200℃):||(10.5±1.0)x10-6K-1||3-point Bending Strength After Sintering (MPa):||1100Mpa|
|Average Transmittance (1.0±0.02mm):||23~35%||Chemical Solubility After Sintering (μg/cm2):||< 100|
|Radioactivity After Sintering (Bq/g):||<0.1||Sintering Temperature (℃):||1450-1550℃Recommended 1530℃|
Colored Dental Zirconia Blank Compatible Milling Zirconium with B2
Upcera Zr-block can be machined to dental restorations by different CNC or manual milling systems. Applications include both anterior and posterior single tooth or bridge restorations. Upcera Zr- block is a partially sintered 3mol% yttria (Y2O3) stabilized zirconia (ZrO2) block, which is made from zirconia ceramics powder by cold isostatic pressing and machining. It is more homogeneous than uniaxial pressed. After fully densified, Zr-block has a high strength, excellent biocompatibility and aesthetics.
UPCERA has been the No.1 and leading manufacturer of dental restorative materials in China. With an investment of tens of millions RMB in Shenyang and Benxi, UPCERA has built a huge modern manufacturing center.
UPCERA also is an industry-leading provider of innovative CAD/CAM system solution in China. We can provide the best CAD/CAM solution for you at the best cost. The future of dental technology is digital. UPCERA has invested a lot in the digital dental technology platform.