Name: 98x14mm CAD/CAM Machine Translucent Zirconia Disc CIP
Brand: UPCERA
SKU: TT-White

98x14mm CAD/CAM Machine Translucent Zirconia Disc CIP

Product Details:

Place of Origin:	CHINA
Brand Name:	UPCERA
Certification:	CE、 FDA 、CFDA、KFDA
Model Number:	TT-White

Payment & Shipping Terms:

Minimum Order Quantity:	2
Price:	Negotiation
Packaging Details:	Carton
Delivery Time:	10 working days after received your payment
Payment Terms:	T/T

Contact Now

Detailed Product Description

Density Before Sintering (g/cm3):	>2.8	Density Aftetr Sintering (g/cm3):	≥6.0
CTE After Sintering (25-200℃):	(10.5±1.0)x10-6K-1	3-point Bending Strength After Sintering (MPa):	> 600
Average Transmittance (1.0±0.02mm):	49%	Chemical Solubility After Sintering (μg/cm2):	< 100
Radioactivity After Sintering (Bq/g):	<0.1	Sintering Temperature (℃):	1430-1470 Recommended 1450
High Light:	CAM Machine Translucent Zirconia Disc , 98x14mm Translucent Zirconia Disc , CIP Zirconia Dental Block

Overview

Quick Details

Place of Origin:: Guangdong, China

Model Number:: TT

Power Source:: Machinery

Warranty:: 1 Year, 12 Months

After-sale Service:: Online technical support

Material:: ceramics, Ceramics

Shelf Life:: 1years

Quality Certification:: ce

Instrument classification:: Class II

Safety standard:: None

Type:: Denture Material

Function:: Top Translucent

Brand:: Upcera

Color:: white

Packing:: 1pcs / box

thickness:: 12mm

Usage:: Veener

Packaging & Delivery

Selling Units:: Single item

Single package size:: 16.5X13X4.5 cm

Single gross weight:: 0.500 kg

Package Type:: Carton

Picture Example:

Lead Time :

Quantity(Pieces)	1 - 100	>100
Est. Time(days)	15	To be negotiated

Product Description

Case Presentation

Detailed Images

Company Introducton

Exhibition

Certifications

Packing & Delivery

Tag:

zirconium in dentistry,

cad cam blocks,

zirconia blocks for cerec

Contact Details

Shenzhen Upcera Dental Technology Co., Ltd.

Contact Person: sales

Tel: +8613438862501

Other Products

HT White High Translucent Zirconia Blank For Open CAD / CAM System

Density before sintering (g/cm3): 3.1±0.5 g/cm3

Density after sintering (g/cm3): 6.07±0.01 g/cm3

CTE after sintering (25-200℃): (10.5±1.0)x10-6K-1

3-point bending strength after sintering (MPa): 1400Mpa

ST White Dental Zirconia Blank 16 Shades Upcera System Compatible

Density before sintering (g/cm3): 3.1±0.5 g/cm3

Density after sintering (g/cm3): 6.08±0.01 g/cm3

CTE after sintering (25-200℃): (10.5±1.0)x10-6K-1

3-point bending strength after sintering (MPa): 1200Mpa

Wieland System High Translucent Zirconia Discs OD 98mm

Density before sintering (g/cm3): 3.1±0.5 g/cm3

Density after sintering (g/cm3): 6.08±0.01 g/cm3

CTE after sintering (25-200℃): (10.5±1.0)x10-6K-1

3-point bending strength after sintering (MPa): 1200Mpa

Zirconia Blocks Dental Translucent Shade CE FDA CFDA Certificated

Density before sintering (g/cm3): 3.1±0.5 g/cm3

Density after sintering (g/cm3): 6.08±0.01 g/cm3

CTE after sintering (25-200℃): (10.5±1.0)x10-6K-1

3-point bending strength after sintering (MPa): 1200Mpa

Dental CAD CAM 1200Mpa High Translucent Zirconia HT Blocks

CTE after sintering (25-200℃): (10.5±1.0)x10-6K-1

Density before sintering (g/cm3): 3.1±0.5 g/cm3

3-point bending strength after sintering (MPa): 1200Mpa

Average transmittance (1.0±0.02mm): 23~35%

Cerec Zirconia Blocks 98×12 mm Low Radioactive For Porcelain Crown

Density before sintering (g/cm3): 3.1±0.5 g/cm3

Density after sintering (g/cm3): 6.08±0.01 g/cm3

CTE after sintering (25-200℃): (10.5±1.0)x10-6K-1

3-point bending strength after sintering (MPa): 1200Mpa

KFDA 100μG/Cm2 High Translucent Zirconia In Dentistry ST White Blank

Density before sintering (g/cm3): 3.1±0.5 g/cm3

Density after sintering (g/cm3): 6.08±0.01 g/cm3

CTE after sintering (25-200℃): (10.5±1.0)x10-6K-1

3-point bending strength after sintering (MPa): 1200Mpa