| Place of Origin: | China |
| Brand Name: | UPCERA |
| Certification: | CE、 FDA 、CFDA、KFDA |
| Model Number: | ST-White |
| Minimum Order Quantity: | 2 |
|---|---|
| Price: | Negotiation |
| Packaging Details: | Carton |
| Delivery Time: | 10 working days after received your payment |
| Payment Terms: | T/T |
| Density Before Sintering (g/cm3): | 3.1±0.5 G/cm3 | Density After Sintering (g/cm3): | 6.08±0.01 G/cm3 |
|---|---|---|---|
| CTE After Sintering (25-200℃): | (10.5±1.0)x10-6K-1 | 3-point Bending Strength After Sintering (MPa): | 1200Mpa |
| Average Transmittance (1.0±0.02mm): | 43% | Chemical Solubility After Sintering (μg/cm2): | < 100 |
| Radioactivity After Sintering (Bq/g): | <0.1 | Sintering Temperature (℃): | 1450-1550℃Recommended 1530℃ |
| High Light: | cad cam blocks,zirconium in dentistry |
||
Zirconia Blocks Dental Translucent Shade CE FDA CFDA Certificated
Description:
| Cerac in lab(Sirona) | U14S | 14-13-13 |
| U20S | 20-14-15 | |
| U20LS | 20-19-15 | |
| U40S | 40-14-15 | |
| U40LS | 40-19-15 | |
| 55-19-15 | ||
| U55S | 55-19-15 | |
| U65S | 65-25-22 | |
| U65LS | 65-40-22 | |
| U85LS | 85-40-22 |
|
|
ST -Color |
|
Density before sintering (g/cm3) |
|
|
Density after sintering (g/cm3) |
|
|
CTE after sintering (25-200℃) |
|
|
3-point bending strength after sintering (MPa) |
|
|
Accelerate aging surface monoclinic phase content |
< 15% |
|
Average transmittance (1.0±0.02mm) |
|
|
Chemical solubility after sintering (μg/cm2) |
< 100 |
|
Cytotoxicity test |
0 level |
|
Radioactivity after sintering (Bq/g) |
|
|
Sintering temperature (℃) |
|
|
|
ST Color |
|
crown |
√ |
|
Bridge |
√ |
|
3-4 units bridge |
√ |
|
5-6 units bridge |
√ |
|
Bridges over 7 units |
√ |
|
Cantilever bridge |
√ |
|
Inlay bridge |
√ |
|
Maryland bridge |
√ |
|
Telescopic crown |
√ |
|
Personalized abutment |
√ |
Our zirconia discs and blocks are made from the zirconia powder which is of superior quality. Our raw material includes high translucent and super translucent zirconia ceramic powder.
The methods used in making our products are compression molding process and cold isostatic pressing process. After cold isostatic pressing, uniform and compact zirconia ceramic blocks are produced, which are very homogenous, high-strength, have excellent biocompatibility and aesthetics.
Contact Person: sales
Tel: +8613438862501
Multilayer Dental Zirconia Blocks CE ISO FDA Certificated Zirconia Dental Material
Dental Laboratory Milling Supplies Zirconia CAD CAM Blank TT White 49% Translucent
Cerec Zirconia Blocks Manul Milling System Compatible For Zirconium Dental Crowns
Cerec Zirconia Blocks 98×12 mm Low Radioactive For Porcelain Crown
ST White Blank High Translucent Zirconia Dental For Open System 16 Shades
ST White Dental Zirconia Blank 16 Shades Upcera System Compatible
Dental Zirconia Blank HT Blocks High Translucent for Open CAD / CAM System
Pre Sintered Dental Zirconia Blank St Multilayer For Sirona System
Super Transparent Dental Zirconia Blank 16 Colors Without Coloring Liqiuids