| Density Before Sintering (g/cm3): | 3.1±0.5 G/cm3 | Density After Sintering (g/cm3): | 6.08±0.01 G/cm3 |
|---|---|---|---|
| CTE After Sintering (25-200℃): | (10.5±1.0)x10-6K-1 | 3-point Bending Strength After Sintering (MPa): | 1100Mpa |
| Average Transmittance: | 25~39% | Chemical Solubility After Sintering (μg/cm2): | < 100 |
| Radioactivity After Sintering (Bq/g): | <0.1 | Sintering Temperature (℃): | 1450-1550℃Recommended 1530℃ |
| High Light: | zirconium dioxide ceramic,dental zirconia sintering furnace |
||
Super Translucent Pre Sintered Zirconia Discs 1100Mpa with A1 A2 A3
specifications
| Cerac in lab(Sirona) | U14S | 14-13-13 |
| U20S | 20-14-15 | |
| U20LS | 20-19-15 | |
| U40S | 40-14-15 | |
| U40LS | 40-19-15 | |
| 55-19-15 | ||
| U55S | 55-19-15 | |
| U65S | 65-25-22 | |
| U65LS | 65-40-22 | |
| U85LS | 85-40-22 |
| ZZ CAD/CAM | D95-10 | |
| D95-12 | ||
| D95-14 | ||
| D95-16 | ||
| D95-18 | ||
| D95-20 | ||
| D95-22 | ||
| D95-25 | ||
| D95-30 |
Indications
|
|
ST Color |
|
crown |
√ |
|
Bridge |
√ |
|
3-4 units bridge |
√ |
|
5-6 units bridge |
√ |
|
Bridges over 7 units |
√ |
|
Cantilever bridge |
√ |
|
Inlay bridge |
√ |
|
Maryland bridge |
√ |
|
Telescopic crown |
√ |
|
Personalized abutment |
√ |
Introduction
Raw material control- Safe and healthy
We believe that the quality control of raw materials is very important and will influence the quality of zirconia blanks directly. We persist in cooperating with well-known zirconia powder manufacturers, choose the best biological nano zirconia powder that meets all international authoritative standards. It is safe and healthy, being stabilized with yttrium during production, and a remarkable aging performance is ensured.
CIP (cold isostatic pressing) molding-homogeneous structure
Cold isostatic pressing is used in molding zirconia powder to achieve a homogeneous structure of the blank, together with perfect micro structure, which ensures a precise sintering shrinkage of zirconia blank and it is suitable for fast milling.
All technical parameters of the zirconia blank are recorded automatically in each production process
Sample milling test is performed from on batch of material
Each batch is tested for sintering performance
Each batch of products have to pass a strict quality spot check
Contact Person: sales
Tel: +8613438862501
Multilayer Dental Zirconia Blocks CE ISO FDA Certificated Zirconia Dental Material
Dental Laboratory Milling Supplies Zirconia CAD CAM Blank TT White 49% Translucent
Cerec Zirconia Blocks Manul Milling System Compatible For Zirconium Dental Crowns
Cerec Zirconia Blocks 98×12 mm Low Radioactive For Porcelain Crown
ST White Blank High Translucent Zirconia Dental For Open System 16 Shades
ST White Dental Zirconia Blank 16 Shades Upcera System Compatible
Dental Zirconia Blank HT Blocks High Translucent for Open CAD / CAM System
Pre Sintered Dental Zirconia Blank St Multilayer For Sirona System
Super Transparent Dental Zirconia Blank 16 Colors Without Coloring Liqiuids