Name: 16 shades Multilayer Zirconia Based Ceramics for Zirconium Oxide Dental Anterior / Posterior
Brand: UPCERA
SKU: TT-LT

Home Products Multilayer Zirconia

16 shades Multilayer Zirconia Based Ceramics for Zirconium Oxide Dental Anterior / Posterior

Product Details:

Place of Origin:	CHINA
Brand Name:	UPCERA
Certification:	CE、 FDA 、CFDA、KFDA
Model Number:	TT-LT

Payment & Shipping Terms:

Minimum Order Quantity:	2
Price:	Negotiation
Packaging Details:	Carton
Delivery Time:	10 working days after received your payment
Payment Terms:	T/T

Contact Now

Detailed Product Description

Density Before Sintering (g/cm3):	>2.8	Density Aftetr Sintering (g/cm3):	≥6.0
CTE After Sintering (25-200℃):	(10.5±1.0)x10-6K-1	3-point Bending Strength After Sintering (MPa):	> 600
Average Transmittance (1.0±0.02mm):	49%	Chemical Solubility After Sintering (μg/cm2):	< 100
Radioactivity After Sintering (Bq/g):	<0.1	Sintering Temperature (℃):	1430-1470 Recommended 1450
High Light:	100μg/cm2 Pre Shaded Zirconia , TT White Pre Shaded Zirconia , CFDA Zirconium Dental Crowns Ceramics

Overview

Quick Details

Place of Origin:: Liaoning, China

Model Number:: TT-ONE

Power Source:: Electric

Warranty:: 1 Year

After-sale Service:: Online technical support

Material:: ceramic, Ceramics

Shelf Life:: 1years

Quality Certification:: ce

Instrument classification:: Class II

Safety standard:: MOL

Brand:: Upcera

thickness:: 18mm

Type:: Denture Material

Color:: multilayer

Usage:: Crown bridge and Coping

Packing:: 1pcs / box

Packaging & Delivery

Selling Units:: Single item

Single package size:: 16.5X13X4.5 cm

Single gross weight:: 0.500 kg

Package Type:: Carton

Picture Example:

Lead Time :

Quantity(Pieces)	1 - 100	>100
Est. Time(days)	30	To be negotiated

Product Description

Case Presentation

Detailed Images

Company Introducton

Exhibition

Certifications

Packing & Delivery

Tag:

zirconium dioxide ceramic,

dental zirconia sintering furnace,

zirconia sintering furnace

Contact Details

Shenzhen Upcera Dental Technology Co., Ltd.

Contact Person: sales

Tel: +8613438862501

Other Products

Super Translucent 1100Mpa Pre Shaded Zirconia Discs A1 A2 A3

Density before sintering (g/cm3): 3.1±0.5 g/cm3

Density after sintering (g/cm3): 6.08±0.01 g/cm3

CTE after sintering (25-200℃): (10.5±1.0)x10-6K-1

3-point bending strength after sintering (MPa): 1100Mpa

High Translucent 3.1g/cm3 Pre Shaded Zirconia Discs Open System

Density before sintering: 3.1±0.5g/cm3

Radioactivity after sintering: <0.1(Bq/g)

Sintering temperature: 1450-1550℃Recommended 1530℃

Density after sintering: 6.08±0.01 g/cm3

ST 16 High Translucency Zirconia Pre - Shaded For Open System

Density before sintering (g/cm3): 3.1±0.5 g/cm3

Density after sintering (g/cm3): 6.08±0.01 g/cm3

CTE after sintering (25-200℃): (10.5±1.0)x10-6K-1

3-point bending strength after sintering (MPa): 1200Mpa

ST Multilayer Yttria Stabilized Zirconia Ceramic For Wieland System

Density before sintering (g/cm3): 3.1±0.5 g/cm3

CTE after sintering (25-200℃): 6.08±0.01 g/cm3

3-point bending strength after sintering (MPa): 1100Mpa

Chemical solubility after sintering (μg/cm2): < 15%

C2 Low Radioactivity 1100Mpa Multilayer Zirconia Full Yttrium Stabilized

Density before sintering: 3.1±0.5 g/cm3

CTE after sintering (25-200℃): 6.08±0.01 g/cm3

3-point bending strength after sintering: 1100Mpa

Cytotoxicity test: < 100

Dental Blanks 1100Mpa 3.1g/Cm3 Zirconium Oxide Ceramic CFDA

Density before sintering (g/cm3): 3.1±0.5 g/cm3

CTE after sintering (25-200℃): 6.08±0.01 g/cm3

3-point bending strength after sintering (MPa): 1100Mpa

Chemical solubility after sintering (μg/cm2): < 15%

1100Mpa Pre Sintered Zirconium Oxide Ceramic

Density before sintering (g/cm3): 3.1±0.5 g/cm3

CTE after sintering (25-200℃): 6.08±0.01 g/cm3

3-point bending strength after sintering (MPa): 1100Mpa

Chemical solubility after sintering (μg/cm2): < 15%